铜基钎料

我公司的HL105、HL801等铜锌钎料，浸润性好、延伸率大、接头剪切强度和抗拉强度高。适用于硬质合金刀具和钎头、钎具、截齿等的钎焊。钎焊产品使用寿命长，能承受大的冲击载荷和疲劳载荷。

咨询热线：: 0730-5631131

详情

　　产品说明：

　　1 铜锌钎料

　　1.1 使用说明

　　铜锌钎料可采用浸渍钎焊、感应钎焊、气体火焰钎焊、炉中钎焊等工艺方法，钎焊前须对母材表面进行清除氧化膜、油脂、尘物处理，并充分预热。

　　感应钎焊时，钎料和钎剂要在装配前安置好，切忌使钎料呈封闭环，防止钎料本身产生感应电流而过早熔化产生虚焊、缺焊。

　　盐浴浸沾钎焊应定期对盐浴液脱氧并予以调整成分。

　　Copper base braze welding material

　　1 Cu-Zn braze welding material

　　1.1 Guideline

　　Cu-Zn braze welding material HL105 and HL801 have good invasion property, extensibility property, shear strength property of joint and strength of extension. They can be used for braze welding of cemented carbide tools, drilling bits and bits. These bits can get long working life, better impact load and fatigue load.

　　Cu-Zn braze welding materials can use techniques such as dip brazing, induction brazing, flame brazing and furnace brazing, the matrix should be clean up and pre-heating before welding.

　　Braze welding materials and brazing flux should in place before induction brazing, the braze welding materials must avoid closed hoop in case of generate inductive current to cause quality problems.

　　Salt-bath brazing techinque should deoxidize the salt liquid and make ajustment for composition.

　　1.2 型号、代号、熔化温度、化学成分

　　牌号企业代号熔化温度化学成分（%）

牌号	企业代号	熔化温度	化学成分（%）
			Cu	Mn	Zn	Co	杂质总量(≤)
BCu58ZnMn	HL105	890-950℃	57-59	3.5-4.5	余量		0.5
BCu57ZnMnCo	HL801	890-930℃	55-57	3.5-4.5	余量	1.5-2.5	0.5
BCu58ZnMnCo	HL811	890-920℃	57-59	3.5-4.5	余量	0.8-1.5	0.5

　　1.2 Grade, code, melting temprature and chemical composition.

Grade	Code	Melting temprature	Chemical composition（%）
			Cu	Mn	Zn	Co	Impurity (≤)
BCu58ZnMn	HL105	890-950℃	57-59	3.5-4.5	Surplus		0.5
BCu57ZnMnCo	HL801	890-930℃	55-57	3.5-4.5	Surplus	1.5-2.5	0.5
BCu58ZnMnCo	HL811	890-920℃	57-59	3.5-4.5	Surplus	0.8-1.5	0.5

　　1.3 供应规格丝状：Φ1.6~Φ6.0×1000mm 片状：L×W×(δ0.1~δ5)mm,长L、宽W根据用户要求。可供圆片、V形、弧形、四边形、多边形等各种形状，规格。 1.3 Specification

　　Filament: Φ1.6~Φ6.0×1000mm

　　Lamella: L×W×(δ0.1~δ5)mm, the L and W according to the client’s request.

　　Disk, V-shape, Arc, quadrangle, polygon, etc.

　　2铜磷钎料和铜银磷钎料

　　2.1 使用说明

　　铜磷钎料和铜银磷钎料适用于气体火焰钎焊、感应钎焊、炉内钎焊、电阻钎焊和浸渍钎焊等工艺方法。

　　化学成分按GB/T6418-1993标准执行，可供应双方协议认可的其它成分的钎料。

　　2.Copper-phosphorus base braze welding material and Copper-silver-phosphorus base braze welding material.

　　2.1 Guideline

　　Copper-phosphorus base braze welding material and Copper-silver-phosphorus base braze welding material can used for flame brazing, induction brazing, furnace brazing, resistance brazing, dip brazing.

　　Chemical composition according to GB/T6418-1993 and also according to client’s request.

　　2.2 技术要求：表（1）铜磷钎焊

产品型号	化学成分						熔点（℃）		规格	特性与用途
	Cu	P	Sb	Sn	Ni	杂质总量	固相线	液相线
BCu93P	余量	6.8-7.5				≤0.10	710	790	条、丝、环、扁	流动性能好，适用于空调电机、仪表行业铜与铜合金钎焊
BCu92SbP		5.8-6.7	1.5-2.5		0.4-1.2		720	800	条、丝	有较好的塑性，适用于铜与铜合金的钎焊，特别适用于电阻钎焊
BCu86PSn		5.8-6.6		6.5-7.0			620	660	条、丝	熔点低，流动性好，适用于焊接电机，电器产品中的铜及铜合金
BCu90SnP		0.5-1.8		8.5-10			930	980	丝、环	熔点低，流动性好，可部分代替银钎料

　　2.2 Technical Requirements: Tab (1) Copper-phosphorus base braze welding material

Grade	Chemical composition						Melting temprature（℃）		Specification	Properties and application
	Cu	P	Sb	Sn	Ni	Impurity	Solidus	Liquidus
BCu93P	Surplus	6.8-7.5				≤0.10	710	790	Strip, filament, round, flat	Good fluidity, used for electrical machine in air-conditon, copper and copper alloy braze welding in instrument
BCu92SbP		5.8-6.7	1.5-2.5		0.4-1.2		720	800	strip, filament	Good plasticity, used for copper and copper alloy braze welding, resistance brazing.
BCu86PSn		5.8-6.6		6.5-7.0			620	660	strip, filament	Low melting temprature, good fluidity; used for welding electrical machine and the copper alloy in electric appliance
BCu90SnP		0.5-1.8		8.5-10			930	980	filament, round	Low melting temprature, good fluidity, replaced some silver braze welding materials.

　　表（2）铜银磷钎料

产品型号	化学成分					熔点（℃）		规格	特性与用途
	Cu	Ag	P	杂质总量	Zn	固相线	液相线
BCu91PAg	余量	1.8-2.2	6.6-7.3	≤0.1		645	790	丝、环、扁	工艺性、流动性好，适用于空调予置环及冰箱电机行业铜及合金钎焊
BCu90PAg		2.8-3.2	6.6-7.3			645	790	丝、环、扁	工艺性、流动性好，适用于空调予置环及冰箱电机行业铜及合金钎焊
BCu89PAg		4.8-5.2	6.3-7.0			645	810	丝、环、扁	在钎焊温度下有极好的流动性，能渗入极小间隙中
BCu88PAg		5.8-6.2	6.3-7.0			645	810	丝、环、扁	工艺性好，适用于钎焊电机，仪表眼镜行业中的铜及铜合金
BCu80PAg		14.5-15.5	4.8-5.3			645	815	丝、环、扁	接头塑性，导电性明显提高，焊接装配要求不高。适用于承受较小振动载荷的铜及铜合金工件钎焊

　　Tab(2) Copper-silver-phosphorus base braze welding material

Grade	Chemical coposition					Melting temprature（℃）		Specification	Properties and application
Grade	Cu	Ag	P	Impurity	Zn	Solidus	Liquidus	Specification	Properties and application
BCu91PAg	Surplus	1.8-2.2	6.6-7.3	≤0.1		645	790	filament, round, flat	Good manufacturability and good fluidity, used for copper and copper alloy braze weling in air-condition and refrigerator
BCu90PAg		2.8-3.2	6.6-7.3			645	790	filament, round, flat	Good manufacturability and good fluidity, used for copper and copper alloy braze weling in air-condition and refrigerator
BCu89PAg		4.8-5.2	6.3-7.0			645	810	filament, round, flat	Good fluidity and can permeate to small slit
BCu88PAg		5.8-6.2	6.3-7.0			645	810	filament, round, flat	Good manufacturability, used for electrical machine in braze welding, copper and copper alloy in instrument and glasses
BCu80PAg		14.5-15.5	4.8-5.3			645	815	filament, round, flat	Good electroconductibility and Good plasticity of the joint, low request of welding. Can used for copper and copper alloy braze welding to bear low vibration load.